| 產(chǎn)品展示 >> FUCHS RENOLIT CXI 2 |
|
FUCHS RENOLIT CXI 2詳細(xì)說明?。g覽1971次）
RENOLIT CXI 2
|
|
 |
Calcium Complex Grease for Severe Conditions
|
|
RENOLIT CXI 2 was developed to work under severe conditions in roller and plain bearings in steel mills, paper industry, mining, concrete, quarries, construction equipment.
RENOLIT CXI 2 should be used for all lubricating points requiring a high performance concerning water resistance, working stability, EP and AW properties.
RENOLIT CXI 2 is easily pumpable even in long tubes, feed by centralized lubricating systems.
RENOLIT CXI 2 is a optimized Calcium-Complex thickened grease based on selected base oils.
RENOLIT CXI 2 shows very good characteristics concerning water resistance, even concerning acids and alkaline solutions, working stability, corrosion protection and oil bleeding.
Characteristics:
| Properties |
Unit |
Value |
Test method |
| Thickener |
|
lithium soap |
|
| Temperature range |
°C |
- 20 to 160 |
|
| Dropping point |
°C |
190 |
ISO 2176/ASTM D 566 |
| NLGI grade |
|
2 |
|
| Worked penetration |
0.1 mm |
265 - 295 |
ISO 2137/ASTM D 217 |
| Working stability, difference after 100,000 strokes |
0.1 mm |
<15 |
ISO 2137/ASTM D 217 |
| Water-spray-off |
% |
5 |
ASTM D 4049 |
| Water-wash-out at 40 °C |
% |
0,5 |
IP 215 |
| Rust inhibiting properties SKF-Emcor with 3% NaCl |
degree of corrosion |
0 and 1 |
DIN 51802/IP 220 |
| Base oil viscosity at 40°C |
mm2/s (cSt) |
app. 300 |
ISO 3104/ASTM D 445 |
| Oil separation at 40 °C/18h |
% Wt. |
<0,1 K |
DIN 51817/IP 121 |
| Oil separation at 120 °C/7h |
% Wt. |
<1 |
DIN 51817/IP 121 |
| Four ball EP-test, weld load |
N |
>5000 |
ASTM D 2596 |
| Timken OK load |
lbs. |
55 |
ASTM D 2509 |
| DIN classification |
|
KP 2 P-20 |
DIN 51825 |
| ISO classification |
|
L-XBEIB 2 |
ISO 6743-9 |
|